[QUOTE=Howard Klepper] Wenge is just fine acoustically. But it is very splitty, has huge pores, and it will spit splinters at you just for spite. I no longer list it among the available woods on my website. Life is too short.[/QUOTE]
| Official Luthiers Forum! http://w-ww.luthiersforum.com/forum/ |
|
| wenge http://w-ww.luthiersforum.com/forum/viewtopic.php?f=10102&t=14712 |
Page 1 of 1 |
| Author: | jonhfry [ Tue Nov 27, 2007 10:01 am ] |
| Post subject: | |
I got a deal on some wenge about a month ago. I am gonna put together some ribs this weekend. This stuff does not have pores, it seems to have craters :) So I am concerned about how it will hold up. For those of you that have built with it, what should I shoot for on the sides for bending thickness? I also have a set of padouk to bend, I already cracked one side at about 0.080, but have enough to make more sides. What thickness do you use for padouk? That stuff is way brittle. |
|
| Author: | Steve Walden [ Tue Nov 27, 2007 10:59 am ] |
| Post subject: | |
Jon - Are you using a heat blanket? I have one you can borrow if you need. |
|
| Author: | joelThompson [ Tue Nov 27, 2007 11:05 am ] |
| Post subject: | |
The wenge should be ok at 0.079 it bends ok no where near as bad as paduak. With the paduak take it down to 0.074 it will realy make all the diference. Just make sure you use good speaders and brace up the sides. If you are still having trouble thin the waist a touch more (0.070) And most of all take your time. Good luck, Joel. |
|
| Author: | Tim McKnight [ Tue Nov 27, 2007 12:47 pm ] |
| Post subject: | |
I just bent a cutaway at .060" and it broke. Arrrgh. |
|
| Author: | Howard Klepper [ Tue Nov 27, 2007 1:16 pm ] |
| Post subject: | |
Wenge is just fine acoustically. But it is very splitty, has huge pores, and it will spit splinters at you just for spite. I no longer list it among the available woods on my website. Life is too short. |
|
| Author: | Blanchard [ Tue Nov 27, 2007 1:56 pm ] |
| Post subject: | |
I have bent cutaways in wenge by hand on a pipe at .090. It is somewhat stiff and reluctant to bend but it can be persuaded if you take your time. One nice thing is that it is very predictable. It tends to produce nice smooth bends with little tendency to "flake up". Mark |
|
| Author: | Bill Greene [ Tue Nov 27, 2007 1:59 pm ] |
| Post subject: | |
[QUOTE=Howard Klepper] Wenge is just fine acoustically. But it is very splitty, has huge pores, and it will spit splinters at you just for spite. I no longer list it among the available woods on my website. Life is too short.[/QUOTE]
|
|
| Author: | Bruce Dickey [ Tue Nov 27, 2007 2:20 pm ] |
| Post subject: | |
Each time I picked up a plank of this stuff, it convinced me to put it back down. Ever tried hugging a porcupine? Me neither. Good to know it'll bend on a pipe. Sorry Tim. I hope you had a matching orphan? |
|
| Author: | MSpencer [ Tue Nov 27, 2007 4:06 pm ] |
| Post subject: | |
If you have any luck with either, let me know, I have not. These are both very difficult woods to work with IMHO. Both are nice looking but ugly to bend. Mike White Oak, Texas |
|